Abstract
Microstructure and phase evolution in Mg-Nd-, Mg-Gd-, and Mg-Gd-Nd-based alloys with additions of Zn, Zr, and Y were analyzed in the as-cast, solution-treated and aged conditions. Close similarity between the as-cast microstructures and precipitation sequence during aging was revealed. Along with this, distinct features of eutectic compounds and of crystal structure, composition, and orientation relationships of β″, β′, and β 1 phases were established. Formation of Zn2Zr3 rods in Mg-Nd-based alloy and cuboid-shaped particles in Mg-Gd- and Mg-Gd-Nd-based alloys is discussed. The features of the age hardening curves were connected with differences between β″ → β′ transformation and different diffusivities of Gd and Nd in Mg-matrix
چکیده
در این تحقیق، ریزساختار وتحول فازی آلیاژهای بر پایه Mg-Nd، Mg-Gd و Mg-Gd-Nd با عناصر آلیاژی Zn، Zr و Y در وضعیتهای ریختگی، محلول‌سازی شده و پیرسازی شده بررسی می شود. شباهت‌های نزدیکی بین ریزساختارهای ریختگی و پیرسازی شده مشاهده گردید. همچنین ویژگیهای متمایز ترکیبات یوتکتیک و ساختار بلوری، ترکیب و روابط جهتگیری فازهایβ″, β′ وβ 1 مشخص شد. پیرامون تشکیل میله های Zn2Zr3 در آلیاژهای پایه Mg-Nd و همچنین تشکیل ذرات مکعبی شکل در آلیاژهای Mg-Gd و Mg-Gd-Nd بحث می شود. ویژگیهای منحنی های پیرسختی به تفاوتهای بین استحاله β″ → β′ و نفوذپذیریهای مختلف Gd و Nd در زمینه ی منیزیم ارتباط داده می شود.
1- مقدمه
آلیاژهای منیزیم حاوی عناصر نادر خاکی به سبب خواص مکانیکی بسیار عالی، مقاومت بسیار خوب در برابر خزش دما بالا، وزن سبک و قابلیت بالای ریخته‌گری تحت فشار در سال های اخیر مورد توجه فراوان قرار گرفته‌اند. حلالیت بالای عناصر نادر خاکی در حالت جامد در زمینه ی منیزیم در دمای بالا و کاهش چشمگیر آن با دما باعث پیر سختی قابل توجه در این آلیاژها حین پیرسازی هم دما در گستره ی دماهای 448K تا 473K درجه سانتی گراد می شود...