Preparation of TiO₂/SiO₂ multilayer flakes and their application to decorative powders were investigated. In contrast to conventional products prepared through the multicoating of core platelets, the coreless TiO₂/SiO₂ multilayer flakes were prepared by detaching multilayer films from their substrates. These flakes exhibited structural colors, when the optical path length of both the TiO₂ and SiO₂ layers are adjusted to be one fourth of the wavelength of visible light. A multicoating of more than five layers resulted in the propagation of cracks, which prevented the preparation of thick flakes. Paint films fabricated using the multilayer flakes and acrylic resins showed reflectance spectra that were comparable with those obtained for multicoatings on substrates

چکیده

آماده سازی ورقه های چند لایه TiO₂/SiO₂ و کاربرد آنها به عنوان پودر تزئینی مورد بررسی قرار گرفته است. در مقایسه با محصولات معمولی تهیه شده از طریق پوشش دهی چند لایه پلاکت های هسته، ورقه های چند لایه TiO₂/SiO₂ با جدا کردن فیلم های چند لایه از زیر لایه های خود آماده می شدند. هنگامی که طول مسیر نوری هر دو لایه TiO₂ و SiO₂ به اندازه یک چهارم طول موج نور مرئی تنظیم شود، این ورقه ها رنگ های ساختاری را به نمایش می گذارند. پوشش چند لایه با تعداد لایه بیش از پنج منجر به گسترش ترک شده، و مانع از آماده سازی ورقه های ضخیم می گردد. فیلم های رنگ ساخته شده با استفاده از ورقه های چند لایه و رزین های اکریلیک طیف بازتابی نشان داد که قابل قیاس با موارد به دست آمده برای پوشش های چند لایه روی بستر می باشد.

1-مقدمه

در طول چند دهه گذشته، روش سل ژل با موفقیت برای ساخت محصولات نوری مانند لنزها، آینه ها و فیلترها به کار برده شده است [1،2]. این روش هزینه های تولید را در مقایسه با روش های دیگر مانند قالب گیری شیشه در درجه حرارت بالا و یا رسوب دادن بخار، کاهش داده است. برای کاربردهای نوری، پوشش های چند لایه اکسید اغلب دارای اهمیت هستند...