Abstract

The catalytic properties of VOx/TiO2 when coated as a thin layer on stainless steel plates figuring out the walls of a reactor were studied in the oxidative dehydrogenation of propane to propene. The method to obtain mechanically stable but catalytically active and selective coatings consisted of dip-coating plates in titanium oxide suspension, followed by grafting of oxovanadium precursor specie in various amounts. In that way the textural and structural properties of coated plates were very similar to those of VOx/TiO2 powders of the same composition as seen from Raman and XPS experiments. The catalytic properties were investigated in a specially designed plate reactor and compared to those of the same catalyst used as powders in a conventional fixed bed reactor. The lower activity of plates vs. powders for the same composition and amount of active phase was attributed to the negative role played by iron diffusing towards the surface and poisoning the vanadate specie

خواص کاتالیزوری VOx/TiO2 زمانی که به شکل یک لایه نازک  بر روی صفحات استیل ضد زنگ پوشش داده شده و به عنوان دیواره های یک راکتور به کار گرفته شده است در هیدروژن زدایی اکسایشی پروپان مورد مطالعه قرار گرفته است. روش بدست آوردن پوشش های مقاوم از نظر مکانیکی اما با فعالیت کاتالیزوری و انتخاب پذیری، شامل غوطه ورسازی صفحات درون سوسپانسیون اکسید تیتانیوم به همراه ایجاد پیوند اجزای پیش ماده اکسی وانادیم در مقادیر مختلف می باشد. در این حالت خواص ساختاری و بافتی صفحات پوشش داده شده بسیار مشابه به پودرهای VOx/TiO2 با ترکیب مشابه بوده اند، همانطور که در آزمایشات رامان و XPS مشاهده شده است. خواص کاتالیزوری در یک راکتور صفحه ای طراحی شده خاص مورد بررسی قرار گرفته و با حالت های مشابه با کاتالیزورهای پودری در راکتور های بستر ثابت متداول مقایسه شده است. فعالیت کم صفحات بر پایه پودرها با ترکیب یکسان و مقدار فاز فعال، به نقش منفی نفوذ آهن داخل سطح و آلوده نمودن اجزای وانادیم نسبت داده می شود.