Silver containing hybrid coatings were synthesized on titanium by sol–gel process. The specimens were studied by transmission electron microscopy, field-emission scanning electron microscopy, bonding test and bacterial counting method. The solid phase content of the sols was increased by the addition of TiO₂ nanoparticles, which avoided the formation of microcracks on the coatings surface. The bonding strength of the coated groups showed a bonding strength improvement of 10.6% compared to the uncoated group. The percent reduction in bacterial count against Staphylococcus aureus seeded on silver containing hybrid coating surface was approximately 99.3% after 24 h incubation, which indicated the strong antibacterial activity of the coating

چکیده

پوشش های ترکیبیی حاوی نقره از طریق فرآیند سل-ژل روی تیتانیوم سنتز شدند. نمونه ها با میکروسکوپ الکترونی عبوری، میکروسکوپ الکترونی روبشی گسیل میدانی، آزمون پیوندی و روش شمارش باکتریایی مورد بررسی قرار گرفتند. محتوای فاز جامد سل با افزایش نانوذرات TiO₂، که از تشکیل ترک های میکرو در پوشش های سطحی جلوگیری کرد، افزایش یافت. استحکام پیوند گروه های پوشش داده شده، بهبود استحکام پیوند برابر 10.6% نسبت به گروه بدون پوشش نشان داد. کاهش درصد تعداد کل باکتری ها در برابر استافیلوکوکوس اورئوس کشت داده شده روی سطح پوشش ترکیبیی حاوی نقره پس از 24 ساعت انکوباسیون حدود 99.3% بود، که نشان دهنده فعالیت قوی ضد باکتری پوشش بود.

1-مقدمه

تیتانیوم یک ماده ترمیمی دندانی جذاب به دلیل داشتن ویژگی های عالی از جمله زیست سازگاری بسیار عالی، استحکام مکانیکی بالا، مقاومت در برابر خوردگی و هزینه پایین است [1]. با این حال، لایه اکسید غیر چسبنده خود تشکیل شونده بر روی تیتانیوم در طول ذوب منجر به چسبندگی ضعیف بین پرسلان- تیتانیوم شده، که کاربرد آن را محدود کرده است [2،3]...